Packaging system for extending the shelf life of food

ABSTRACT

A sealed barrier bag that contains a first compartment, a second compartment, a non-oxidizing gas located in the first compartment, a perishable item located in the second compartment, and a device for venting the non-oxidizing gas from said second compartment.

CROSS-REFERENCE TO RELATED PATENT APPLICATIONS

This application is a continuation-in-part of applicant's copending patent applications U.S. Ser. No. 09/684,381, filed on Oct. 7, 2000, U.S. Pat. No. 6,269,946 B1 which was a continuation-in-part of U.S. Ser. No. 09/609,798, filed on Jul. 3, 2000, U.S. Pat. No. 6,269,945, which was a continuation-in-part of U.S. Ser. No. 09/519,105, filed on Mar. 6, 2000 (now U.S. Pat. No. 6,213,294), which was a continuation-in-part of U.S. Ser. No. 09/342,844, filed on Jun. 29, 1999 (now U.S. Pat. No. 6,112,890). This case is also a continuation-in-part of patent applications U.S. Ser. No. 09/196,450 (filed Nov. 19, 1998, now U.S. Pat. No. 6,210,725) and U.S. Ser. No. 09/182,754 (filed Oct. 29, 1998, now U.S. Pat. No. 6,023,915).

TECHNICAL FIELD

A packaging system for preserving perishable items which comprises a barrier bag with a first compartment, a second compartment, sealed means for closing one end of the first compartment, sealed means for closing one end of the second compartment, a non-oxidizing gaseous material disposed within said first compartment, a perishable item disposed within said second compartment, means for flowing gaseous material from said first compartment to said second compartment, and means for venting said non-oxidizing gaseous material from said second compartment.

BACKGROUND OF THE INVENTION

Applicant's U.S. Pat. No. 6,112,890 describes a packaging system for preserving perishable items; the system of this patent was comprised of a barrier bag. This patent, and prior art cited in it, are the most relevant references known to applicant regarding the technology claimed in this patent application.

It is an object of this invention to provide an improved barrier bag for preserving perishable goods.

SUMMARY OF THE INVENTION

In accordance with this invention, there is provided a packaging system for preserving perishable items which comprises a barrier bag with a first compartment, a second compartment, sealed means for closing one end of the first compartment, sealed means for closing one end of the second compartment, a non-oxidizing gas disposed within said first compartment, a perishable item disposed within said second compartment, means for flowing non-oxidizing from said first compartment to said second compartment, and means for venting carbon dioxide from said second compartment.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be more fully understood by reference to the following detailed description thereof, when read in conjunction with the attached drawings, wherein like reference numerals refer to like elements, and wherein:

FIG. 1 is a sectional view of one preferred packaging system of the invention;

FIGS. 2A, 2B, 2C, 2D, and 2E schematically illustrate one means of preparing and using the packaging system of FIG. 1;

FIG. 3 is a sectional view of a portion of the tray used in the system of FIG. 1;

FIG. 4 is a sectional view of one preferred barrier bag which may be used in the packaging system of FIG. 1;

FIG. 5 is a graph illustrating the oxygen concentrations in a specified packaging material over time with two systems, one of which uses a conventional foam tray, and the other of which uses the open-cell foam tray of this invention;

FIG. 6 is a sectional view of another preferred packaging system of the invention;

FIG. 7 illustrates a process for making a packaging system in which the barrier bag expands during the process;

FIG. 8 illustrates a process for limiting the extent to which the barrier bag can expand during the process;

FIGS. 9A and 9B are schematic representations of one preferred process of the invention utilizing the barrier bag depicted in FIG. 4; and

FIG. 10 is a side view of the final product produced by the process of FIGS. 9A and 9B.

One preferred packaging system of the invention.

FIG. 1 is a sectional view of one preferred packaging system 10 which is comprised of a tray 12 which, in the preferred embodiment depicted, includes flanges 14 around the perimeter of such tray 12. A perishable good or goods 15 is disposed within tray 12.

The perishable goods which may advantageously be protected by the packaging system 10 of this invention include oxygen-sensitive food such as, e.g., red meat (veal, beef, pork, etc.), pasta, cooked food, and the like. Alternatively, one may preserve perishable non-food items such as photographic film, computer components, inorganic materials susceptible to oxidation, etc.

In one preferred embodiment, the goods disposed within the packaging system include red meat which has been processed to remove oxygen from its surfaces and prevent the formation of metmyoglobin. In this embodiment, the red meat disposed within the packaging system contains less than about 10 weight percent, by weight of total pigment in the red meat, of metmyoglobin.

In the preferred embodiment depicted in FIG. 1, a skin layer 19 is contiguous with and attached to the bottom surface of the tray and preferably up the side of the tray to the flanges 14.

In the preferred embodiment depicted in FIG. 1, a gas permeable film material 18, which may include slits or perforations 20, covers the perishable goods 15. This skin layer 19 is illustrated more clearly in FIG. 3.

Referring again to FIG. 1, it will be seen that the tray 12 which is overwrapped with gas permeable film material 18 is disposed within a barrier bag 22 which surrounds the tray 12 and which preferably is made of a substantially impermeable material. This barrier bag is attached to a one-way valve 24, which will be described in greater detail elsewhere in this specification.

From about 10 to about 150 grams of solid carbon dioxide 16, which may be in the form a flakes, one or more pellets, an irregular shape, etc., are disposed outside of tray 12 but within barrier bag 22.

The barrier bag 22, prior to the time it is sealed, contains an opening 23.

FIG. 2A is a sectional view of tray 12 attached to skin layer 19. The tray 12 is comprised of at least 90 weight percent of foam material. In one preferred embodiment, the foam material is open-cell foam which contains at least about 20 volume percent of open cells.

As is known to those skilled in the art, an open-cell cellular plastic is a cellular plastic in which there is a substantial number of interconnected cells; see, e.g., A.S.T.M. D883. Reference also made by had to U.S. Pat. Nos. 5,798,409 (open cell foams of polystyrene and polyurethane), 5,784,845 (open cell foam material made from alkenyl aromatic polymer material), U.S. Pat. No. 5,646,193 (rigid open cell foam material), U.S. Pat. Nos. 5,557,816, 5,475,890, 5,434,024 (open cell foam material of polyvinyl chloride, or polyisocyanate, or polyphenol, or polypropylene), U.S. Pat. Nos. 5,348,587, 5,343,109, 5,239,723, 5,139,477 (polyethylene open cell foam material), U.S. Pat. Nos. 4,739,522, 4,395,342 (open cell foam material made from cellulose acetate, or phenol-fonnaldehyde, or cellular rubber), etc. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

It is preferred that the open cell foam material be made from a resin selected from the group consisting of polyethylene, polyvinyl chloride, polyacrylonitrile (such as the “BAREX” resin sold by the British Petrolem/Amoco company), poly(ethylene terephthalate), polystyrene, rubber-modified polystyrene, ethylenepolystyrene, interpolymers (such as “INDEX” interpolymers sold by Dow Chemical Corporation of Midland Michigan), polypropylene, polyurethane, polyisocyanurate, epoxy, urea formadehyde, rubber latex, silicone, fluropolymer or copolymers thereof or blends thereof, and in general any other suitable resin, resin mixture, or any foamable composition which can be made with an open cell structure such as, e.g., materials made using a silane peroxide catalyst system (sold by the Sentinel Foam company or Hyanis, Mass.).

As is well known to those skilled in the art, one may vary the degree to which a foam material contains open-cell structure by the process taught by applicant in his 1977 article entitled “Controlling the Properties of Extruded Polystyrene Foam.” This article was presented at the Proceedings of the International Conference on Polymer Processing, which was held at the Massachusetts Institute of Technology, Cambridge, Mass, in August 1977. This proceedings were published in 1977 in a book edited by Nam P. Suh and Nak-Ho Sung entitled “Science and Technology of Polymer Processing”(The MIT Press, Cambridge, Mass., 1977); and a description of means to control the concentration of open cells appeared on page 410 of this book. In particular, the correlation between the concentration of open cells produced in the foam and the melt temperature of the resin/blowing agent mixture used, was discussed.

Referring again to FIG. 2A, and in the preferred embodiment depicted therein, the tray 12 is comprised of foam material which contains at least about 20 volume percent of open cells. In one preferred embodiment, the foam material contains at least about 30 volume percent of open cells. It is even more preferred that the foam material contain from about 30 to about 90volume percent of open cells and, even more preferably, from about 45 to about 90 volume percent of open cells. The extent to which a foam material contains open-cell foam may be determined by A.S.T.M. Standard Test D2856-94, “Test Method for Open-Cell Content of Rigid Cellular Plastics by the Air Pycnometer.”

The open-cells in the foam contain a gas phase with gases which are substantially identical to the gases in ambient air. Thus, the open-cells generally contain a gas phase comprised of from about 19 to about 22 volume percent of oxygen (depending upon the altituide) and from about 78 to about 81 volume percent of nitrogen. In general, such gas phase contains from about 20.5 to about 21 volume percent of oxygen and from about 79 to about 79.5 volume percent of nitrogen. However, after the open-cells in the gas tray have been treated by the process of this invention, they preferably contain less than about 0.05 volume percent of oxygen.

FIGS. 2B, 2C, 2D, and 2E illustrate how use the tray depicted in FIG. 2A can be used to make the structure depicted in FIG. 1. For the sake of simplicity of representation, much of the detailed description of the tray contained in FIG. 2A has been omitted from FIGS. 2B, 2C,2D, and 2E.

After the tray 12 has been fabricated (see FIG. 2A), the good or goods 15 are placed in the tray and then wrapped either manually or automatically with a gas permeable film material 18, or other suitable means, to holds the goods 15 in place, thereby forming wrapped tray 30 (see FIG. 2C).

The open-cell foam material which comprises tray 12 have as an average cell diameter of from about 0.0001 to about 0.030 inches and, more preferably, from about 0.002 to about 0.008 inches. In one preferred embodiment, the cell diameter of such cells is from about 0.003 to about 0.007 inches.

The average cell diameter of a foam may be determined in accordance with the procedure described in applicant's U.S. Pat. Nos. 3,953,739 and 4,329,052, the disclosures of which are hereby incorporated by reference into this specification. One may also use one or more of the methods disclosed in other United States patents, such as, e.g., U.S. Pat. Nos. 5,912,729, 5,817,704, 5,810,964, 5,798,065, 5,795,680, 5,790,926, 5,786,401, 5,770,634, 5,7532,717, 5,912,729, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

Referring again to FIG. 1A, the tray 12 has walls with a thickness 21 of from about 0.025 to about 0.5 inches and, preferably, from about 0.040 to about 0.15 inches. In one embodiment, the thickness 21 is from about 0.04 to about 0.1 inches. The thickness of the sidewalls 23 and 25 of tray 12 may be equal to or less than the thickness of the bottom surface 27 of tray 12. In one embodiment, the thickness of sidewall 25 is from 25 to about 50 percent of the thickness of the bottom surface 27.

In one preferred embodiment, illustrated in FIG. 2A, the bottom surface 27 of tray 12 forms an interior angle (29 or 31) between sidewalls 23 or 25 of from about 1 to about 90 degrees and, preferably, from about 25 to about 50 degrees. Angles 29 and 31 may be the same or different.

Referring again to FIG. 2A, the tray 12 preferably has a density of from about 0.1 to about 55 pounds per cubic foot and, preferably from about 1 to about 10 pounds per cubic foot, and more preferably from about 1.5 to about 6 pounds per cubic foot. It is even more preferred that the density be from about 2.0 to about 5.0 pounds per cubic foot. In one embodiment, the density of tray 12 is from about 2 to about 3 pounds per cubic foot.

Referring again to FIG. 2A, it will be seen that tray 12 is attached to a skin 19. The thickness of skin 19 is preferably from about 0.0005 to about 0.01 inches and, more preferably, from about 0.002 to about 0.005 inches.

In FIGS. 2B through 2E, tray 12 is depicted in various combination with other elements. However, for the sake of simplicity of representation, many of the details of tray 12 depicted in FIG. 2A have been omitted in these latter Figures.

As is illustrated in FIG. 2B, the perishable goods 15 are placed within tray 12, either manually or automatically. In one embodiment, not illustrated, an absorbent pad is placed between the goods 15 and the bottom of the tray in order to absorb excess juices exuded from the goods 15.

Referring to FIG. 2C, a gas permeable film material 18 adapted to pass both oxygen and carbon dioxide is wrapped around the entire tray 12. The film material may be adhered to the tray because of its “cling properties,” and/or it may be heat-treated to cause it to adhere to the tray; in each either event, the film 18 is contiguous with the sides and the bottom of tray 12 and encloses the perishable goods 15. Thus, as is disclosed in U.S. Pat. No. 5,698,250, the film 18 may contain additives which allow the film to cling to itself. This film generally has a thickness ranging from about 0.5 mil to about 1.5 mils.

These gas-permeable films are well known to those skilled in the art and are described, e.g., in U.S. Pat. Nos. 5,888,597, 5,885,699, 5,852,152 (ethylene/vinyl acetate film and ethylene/acrylic acid film), U.S. Pat. Nos. 5,840,807, 5,839,593, 5,804,401, 5,780,085, 5,759,712, 4,056,639, 4,011,348, 3,867,558, 3,857,981, 3,728,135, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

In one preferred embodiment, film 18 is a polyvinyl chloride film supplied by the Borden Packaging and Industrial Products company of North Andover, Mass as “Resinite.” This film 18 has an oxygen permeability of from about 1100 to about 1400 cubic centimeters per 100 square inches per 24 hours, as measured by the Mocon Controls Oxtran 100 machine measured at 23degrees Centigrade. The film has a carbon dioxide permeability of from about 12,400 to about 13,4000 cubic centimeters per 100 square inches per 24 hours as measured by a Linde Cell at 23 degrees Centigrade and 1 atmosphere pressure.

In the preferred embodiment depicted in FIG. 2C, film 18 is comprised of perforations 33, 35, 37, and 39. In this embodiment, it is preferred that each of such perforations have a maximum cross-sectional dimensional of less than about 0.05 inches. When such perforations are present, it is preferred that from about 1 to about 4 of them occur per square inch of surface.

Referring to FIG. 2D, the wrapped tray 30 (see FIG. 2C) is wrapped in an oxygen barrier bag 22 which, in the preferred embodiment depicted, is preferably shaped similarly to a typical bag with an open end into which to insert the wrapped tray. Such oxygen barrier bags are well known to those skilled in the art and are described, e.g., in U.S. Pat. Nos. 5,862,947, 5,855,626, 5,811,027, 5,799,463, 5,798,055, 5,780,085, 5,753,182, 5,711,978, 5,700,554, 5,667,827, 5,583,047, 5,573,801, 5,573,797, 5,529,833, 5,350,622, 5,346,644, 5,227,255, 5,203,138, 5,195,305, 4,857,326, 4,605,175, 4,082,829, 3,953,557, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

In one preferred embodiment, the barrier bag described in column 4 of U.S. patent 5,698,250 may be used. This bag is commercially available as product number 325C44-EX861B from the PrintPak, Inc. company of Atlanta, Ga.

In another preferred embodiment, the barrier bag used is a biaxially oriented nylon film coated with an oxygen barrier coating (such as polyvinylidene chloride) and having a thickness of from about 0.00072 to about 0.00112 inches. Such a bag is commercially available from the Allied Signal Corporation (of New Jersey) as “Capron Emblem 1530” or “Capron Emblem 2530.”

In one embodiment, the barrier bag is a shrinkable barrier bag which, after it is disposed over the tray, is caused to shrink by the application of heat. These heat shrinkable barrier bags are well known to those skilled in the art. Reference may be had, e.g., to U.S. Pat. Nos. 6,206,569, 6,045,924, 6,015,235, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

By way of further illustration, one may use the heat shrunk barrier bag disclosed in U.S. Pat. No. 5,916,613, the entire disclosure of which is hereby incorporated by reference into this specification.. Thus, e.g., one may use a barrier bag known as the “B540 (TM) barrier bag, available from W. R. Grace & Co- Conn., of Duncan, S.C. 29334. This barrier bag may be made of heat-shrinkable polyolefins and polyvinylidene chloride, and included a layer of cornstarch (known as C-3-170 Non-Offset Spray Powder (TM) cornstarch, and which, according to the manufacturer, is 99.0% foodstarch, 1% additive, this product being obtained from Varn, of Ridgewood, N.J.), in an amount of about 10 grams per 100 square inches, on the inside surface of the oxygen-impermeable film. The barrier bag was heat-shrunk so that the resulting package was substantially as illustrated in FIG. 1.

In another embodiment, one may use a heat shrinkable barrier bag obtained from the Cryovac Sealed Air Corporation of Duncan, S.C. as product number LS 155 340CF.

Regardless of the particular barrier bag used, it is preferred that it have an oxygen permeability of less than 5 cubic centimeters per 100 square inches per 24 hours, as measured by a suitable gas permeability measuring device, such as the aforementioned Mocon Controls Oxtran 100 machine; measurements are taken under ambient conditions. This test method is well know, being described in A.S.T.M. Standard Test D-1434 “Test Method for Determining Gas Permeability Characteristics of Plastic Film and Sheeting.” Reference may also be had to U.S. Pat. Nos. 5,913,445, 5,882,518, 5,769,262, 5,684,768, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

Referring again to FIG. 2D, the barrier bag 22 is preferably operably connected to a pressure relief valve 24. The pressure relief valve 24 is adapted to open and allow gas disposed within barrier bag 22 when the pressure within barrier bag 22 is from about 0.05 to about 1.0 pounds per square inch gauge and, more preferably, from about 0.1 to about 0.2 pounds per square inch gauge. In an even more preferred embodiment, the valve 24 is adapted to allow gas disposed within barrier bag 22 to vent to the outside when the pressure within such bag is from about 0.12 to about 0.14 pounds per square inch gauge.

The valve 24, after it is has opened to vent gas from the barrier bag 22, closes when the internal pressure drops within the range of from about 0.01 to about 0.04 pounds per square inch gauge.

Pressure sensitive gas valves for releasing gas from a sealed flexible pouch, such as valve 24, are well known to those skilled in the art. See, for example U.S. Pat. Nos. 5,059,036, 5,419,638, 5,048,846, 4,653,661, 4,690,667, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

In one preferred embodiment, the pressure sensitive gas valve is sold by the Plitek, Inc. company of 681 Chase Avenue, Elk Grove Village, Illinois 60007; see, e.g., a publication by Plitek (entitled “Plitek Pressure Relief Valve”) which was published on July 8, 1991. A copy of this publication is in the file history of U.S. Pat. No. 5,419,638 of Mark D. Jamison.

The valve 24 may be incorporated into the gas barrier bag 24 by conventional means such as, e.g., by means of the “CCL Model 230 Valve Applicator labelling system” which is sold by CCL Industries of 3070 Mainway, Units 16-19, Burlington, Ontario L7M3X1. This system is adapted to be secured to the side of a vertical form-fill and seal machine to apply self-adhesive valve labels to the plastic web on the forming tube section of the machine just prior to the seal and cut station.

Referring again to FIGS. 2D and 2E. after the sealed tray 30 is disposed within the barrier bag 22, solid carbon dioxide 16 is charged into the barrier bag 22 prior to the time the bag is sealed. In general, from about 10 to about 150 grams of solid carbon dioxide is charged to barrier bag 22. For a description of one use of such solid carbon dioxide in a barrier bag without a valve 24, reference may be had to U.S. Pat. Nos. 5,731,023 and 5,737,905. The entire disclosure of each of these United States patents is hereby incorporated by reference into this specification. It should be noted that the amount of solid carbon dioxide used in the processes of these patents is substantially less than the amount of carbon dioxide generally used in applicant's process. In general, a sufficient amount of carbon dioxide is used to generate at least about 1.5 liters of gaseous carbon dioxide per kilogram of perishable goods 15; see, e.g., an article by N. Penney and R.G. Bell entitled “Effect of Residual Oxygen on the Colour, Odour and Taste of Carbon-Dioxide-Packaged Beef, Lamb and Pork . . . ” published in Meat Science 33 (1993) at pages 245-252.

Referring to FIG. 2E, after the solid carbon dioxide is disposed within barrier bag 22, the bag is heat sealed by conventional means; see, e.g., U.S. Pat. Nos. 5,908,676, 5,799,463, 5,759,653, 5,332,121, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

In one embodiment, after the barrier bag 22 has been heat sealed, a vacuum is applied through valve 24 to remove air disposed within barrier bag 22.

FIG. 3 is a sectional view, taken through line 3—3 of FIG. 1, of tray 12. Referring to FIG. 3, and to the preferred embodiment depicted therein, it will be seen that tray 12 is comprised of open cell foam 50 to which is attached a skin layer 19 which is preferably comprised of a multiplicity of through-holes 52, 54, 56, 58, 60, and 62. These through holes have a maximum dimension (such as a maximum diameter) of from about 5 to about 40 mils and generally extend from the top surface 64 of the skin layer 19 to the top surface 66 of the open cell foam layer.

In another embodiment, not shown, no such through holes exist in the skin layer 19. In either embodiment, however, the skin layer has a thickness 68 of from about 0.0005 to about 0.01 inches, and, preferably, from about 0.002 to 0.005 inches.

As will be apparent to those skilled in the art, the structure depicted in FIG. 3 is a laminated structure with one or more skin layers 19 and/or 68. Means for producing such a laminated structure are well known. Thus, by way of illustration, in the process of Example 4 of U.S. Pat. No. 4,510,031, a 0.2 millimeter thick sheet of an ethylene/propylene block copolymer having a density of 0.91 was heat laminated to both surfaces of a foamed sheet. Thus, by way of further illustration, laminates made by bonding a skin layer to a foam core are described in U.S. Pat. Nos. 5,882,776, 5,876,813, 3,633,459, and the like. Thus, by way of even further illustration, U.S. Pat. No. 4,098,941 discloses a process in which a skin layer is formed in situ on a foam core by heat treatment. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

The skin layers 19 and/or 68 may be adhered to the foam layer 50 by adhesive means, by heat lamination means, by coextrusion, by mechanical means, and by other conventional means known to those skilled in the art. The skin layer 19 and/or the skin layer 68 may consist essentially of unfoamed plastic (such as polystyrene, or rubber-modified polystyrene, or polyethylene or polypropylene, mixtures thereof, and the like), paper, and the like. In another embodiment, the skin layer 19 and/or the skin layer 68 may consist essentially of either open cell foam and/or closed cell foam.

Without wishing to be bound by any particular theory, applicant believes that the laminated structure possesses substantially more flexural strength than the unlaminated foam core and, in many cases, reaches or exceeds the structural strength of an unlaminated closed cell foam core, such as the ones described in U.S. Pat. No. 5,698,250.

Processes for making closed cell polystyrene foam are well known to those skilled in the art. See, e.g., the following United States patents, each of which named the applicant as an inventor: U.S. Pat. Nos. 5,356,944, 5,286,429, 4,747,983, 4,329,052, 4,022,858, 3,953,739, 3,879,507, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

Processes for modifying closed-cell polystyrene foam processes to make open cell foam are also well known to those skilled in the art. See, e.g., the article by applicant entitled “Controlling the Properties of Extruded Polystyrene Foam” given at the Proceedings of the International Conference on Polymer Processing held at The Massachusetts Institute of Technology, Cambridge, Mass. in August of 1977 which was published in a book entitled “Science and Technology of Polymer Processing,” edited by Nam P. Suh and Nak-Ho Sung (The MIT Press, Cambridge, Mass, 1977). Reference may also be had to U.S. Pat. Nos. 5,798,409, 5,784,845, 5,646,193, 5,557,896, 5,475,890, 5,434,024, 5,343,109, 5,239,723, 5,139,477, 4,739,522, 4,395,342, 4,259,373, 4,108,600, 4,107,876, 4,082,678, 4,079,170, 3,868,716, 3,844,286, 3,589,592, and the like. The disclosure of each of these United States patents is hereby incorporated by reference into this specification.

As is disclosed in these patents, the conventional process for making polystyrene foam, which is described in the aforementioned patents, uses the well documented extrusion process for producing cellular polystyrene foam in which a solution of a volatile blowing agent in molten polymer, formed in an extruder under pressure, is forced through an orifice into an ambient environment of temperature and pressure. The polymer simultaneously expands and cools under conditions that give it enough strength to maintain dimensional stability at the time corresponding to optimum expansion. Stabilization is due to cooling of the polymer phase to a temperature below its glass transition or melting point. Cooling is effected by vaporization of the blowing agent, gas expansion, and heat loss to the environment.

The polystyrene foam sheet thus produced is allowed to equilibrate with atmospheric gases for a period of from about 1 to about 5 days, at which time it is heat shaped into a container using conventional thermoforming equipment.

A Preferred Barrier Bag of the Invention

FIG. 4 is a schematic view of another system for preserving perishable goods in which a two compartment barrier bag comprised of compartment 102 and compartment 104 communicate with each other via an orifice 106.

In the embodiment depicted in FIG. 4, two compartments are depicted, and they are substantially aligned with each other. In another embodiment, not shown, three or more compartments are present in the barrier bag; in one aspect of this embodiment, the third compartment contains a material other than carbon dioxide or perishable goods, such as, e.g., a bacteriostatic agent. In yet another embodiment, the compartments in the barrier bag are not aligned with each other.

In the preferred embodiment depicted in FIG. 4, as will be more clearly described hereinbelow, means are providing for flowing a non-oxidizing gas from one compartment to another compartment. As used herein, the term “non-oxidizing gas”refers to a gas which contains less than about 1 volume percent of oxygen. Thus, such non-oxidizing gases include carbon dioxide, nitrogen, argon, helium, krypton, neon, radon, zenon, ziron, and the like. The preferred non-oxidizing gas is selected from the group consisting of carbon dioxide, nitrogen, and mixtures thereof.

Thus, for example, and referring again to FIG. 4, a chunk of solid carbon dioxide 108 is disposed within compartment 102. This solid carbon dioxide gradually sublimes, causing gaseous carbon to travel via arrows 110 and 112 and, when pressure has built up, to vent through valve 24.

The barrier bag 100 of FIG. 4 is comprised of means for flowing the sublimated carbon dioxide from compartment 102 to compartment 104; in the embodiment depicted, such means include an orifice 106 disposed between compartments 102 and 104. Other means for flowing the gaseous carbon dioxide between compartments 102 and 104 also may be used such as, e.g. a multiplicity of such orifices 106, one or more one-way valves, etc.

The system of this FIG. 4 is very similar to the system depicted in FIG. 1, with the exception that it utilizes a two-compartment barrier bag rather than a single compartment barrier bag, and it does not utilize the tray 30. In the embodiment depicted, the two compartments 102 and 104 are formed by a heat seal 11 which forms a barrier between compartments 102 and 104 except where orifice 106 is present.

In one preferred embodiment, depicted in FIG. 4, an absorbent pad 31 is disposed beneath the goods 15. The absorbent may consist of or be comprised of any material which will absorb fluid from the perishable goods 15. Thus, it may be made out of cotton, absorbent polymeric material, sponge material, open cell foam material, and the like.

In the embodiment depicted in FIG. 4, the barrier bag 100 is open at tops 113 and 115. However, once the solid carbon dioxide 108 and the perishable goods 15 have been disposed within the barrier bag 100, it is preferred to seal tops 113 and 115 to form seals 117 and 119 by the heat sealing means described elsewhere in this specification.

FIG. 5 is a graph presenting data generated from the experiments of the Examples described in applicant's copending patent application 09/342,844.

Another Preferred Packaging System of the Invention

FIG. 6 shows an packaging system 11 which is substantially identical to the packaging system 10 depicted in FIG. 1 but which differs from packaging system 10 in that it contains oxygen absorber 200. In one embodiment, not shown, a similar oxygen absorber is used in the barrier bag depicted in FIG. 4.

One may use any of the commercially available oxygen absorbers as oxygen absorber 200. One preferred oxygen absorber 200 is an iron-based oxygen absorber such as, e.g., the iron-based absorbent described in U.S. Pat. No. 5,928,960. The entire disclosure of this United States patent is hereby incorporated by reference into this specification.

Further reference may be had to U.S. Pat. No. 5,262,375, which also discusses oxygen absorber packets. The entire disclosure of this patent is hereby incorporated by reference into this specification.

One oxygen absorber packet which may be used in the process of this invention is manufactured by Multiform Dessicants Incorporated of North Tonawanda, N.Y. It is believed that this absorber packet contains iron and silica gel.

Other iron-based oxygen absorbers also will work well as oxygen absorber 200.

Referring again to FIG. 6, and in the preferred embodiment depicted therein, the solid carbon dioxide 16 preferably is in particulate form and has a particle size distribution such that at least about 90 weight percent of its particles are sized in the range from about 25 microns to about 1000 microns and, more preferably, are sized in the range of from about 100 to about 500 microns. In one embodiment, at least about 90 weight percent of the carbon dioxide particles are in the range of from 200 to about 400 microns.

In the embodiment depicted in FIG. 6, it is preferred that the barrier bag 22 have an oxygen permeability of less than 10 cubic centimeters per 100 square inches per 24 hours, as measured by suitable gas permeability measuring device.

Referring again to FIG. 6, and in the preferred embodiment depicted therein, the tray 12 preferably has a water absorbency of from about 5 to about 500 percent. In the test used to determine water absorbency, a tray is weighed under ambient conditions and then immersed in water for a period of thirty minutes. Thereafter, the tray is removed from the water bath and weighed. The ratio of the weight of the “wet tray” to that of the “dry tray” is at least about 2.0/1.0 and, preferably, at least 2.5/1.0. A tray with the desired characteristics is commercially available form Vitembal S.A. of Remoulins, France, as the “Integral” absorbent tray. A process of limiting the expansion the barrier bag.

FIG. 7 illustrates the condition of packaging system 11 (see FIG. 6) after the carbon dioxide 16 has sublimated and is released through valve 24. Certain components of packaging system 11 have been omitted from FIG. 7 for the sake of simplicity of representation.

Referring to FIG. 7, it will be seen that barrier bag 22 has a height 202 which is substantially greater than the height of the barrier bag 22 depicted in FIG. 6. As will be apparent to those skilled in the art, this occurs because the sublimation of the solid carbon dioxide produces a gaseous phase which increases the pressure within barrier bag 22. Some of this pressure is vented to atmosphere via valve 24, but some of the pressure causes barrier bag 22 to increase in volume. If the expansion of barrier bag 22 is unrestrained, and depending upon the concentration of the solid carbon dioxide 16, the volume enclosed by barrier bag 22 could increase by as much as 1,500 percent.

When the packaging system 11 has a large volume, it is difficult to ship efficiently and is more cumbersome to use.

FIG. 8 illustrates a process for limiting the increase in volume of the barrier bag 22. Referring to FIG. 8, it will be seen that the solid carbon'dioxide 16 within barrier bag 22 causes sublimate to flow in the direction of arrow 204 through valve 24. It also causes the barrier bag 22 to expand in volume, but such volume expansion is limited by the presence of constraint 206. In the particular embodiment depicted, constraint 206 is comprised of opposing walls 208 and 210 which are separated by distance 202. An orifice 212 disposed within wall 208 is adapted to receive valve 24 and to allow gas passing through valve 24 to exit the constraint 206. Depending upon the extent of distance 202, the extent to which the barrier bag 22 will be allowed to expand during sublimation of the solid carbon dioxide 16 can be controlled.

One may use any suitable means for controlling the expansion of the volume within barrier bag 22. In one embodiment, not shown, wall 208 is hingeably attached at point 214 to wall 209 and may be rotated upwardly in the direction of arrow 216 and/or downwardly in the direction of arrow 218, thereby varying the effective distance 202 between wall 208 and wall 210 at various points along such wall. Other suitable means for controlling the expansion of the volume within barrier bag 22 will be apparent to those skilled in the art.

In one embodiment, the restraining means is comprised of shrink film which is used as the barrier bag 22 (see, e.g., FIG. 1). This shrink film barrier bag 22 is preferably oxygen-impermeable. Some suitable oxygen-impermeable shrink films are described, e.g., in U.S. Pat. Nos. 5,645,788, 5,482,770, 5,376,394, 5,302,402, 5,035,8512 4,894,107, and the like. The disclosure of each of these United States patents is hereby incorporated into this specification.

As will be apparent, once the shrink film barrier bags 22 are heat treated, they resist deformation by gas pressure, thereby effectively reducing the volume of the system and restraining expansion of the package.

Referring again to FIG. 8, and in the preferred embodiment depicted therein, the packaging device 11 constrained by constraint 206 is disposed within a vacuum chamber 300 comprised of a port 302. Sublimate exiting constraint 206 through valve 24 then can exit vacuum chamber 300 through valve 304 in the direction of arrow 306.

As will be apparent to those skilled in the art, the presence of a vacuum within vacuum chamber 300 facilitates the removal of oxygen from barrier bag 22. It is preferred that the vacuum within vacuum chamber 300 be less than 10.0 millimeters of mercury absolute. This will cause the pressure within barrier bag to be less than about 10.0 millimeters of mercury absolute.

A Preferred Process of this Invention

FIGS. 9A and 9B are schematic representations of a preferred process of this invention which utilizes the barrier bag 100 of FIG. 4. In these Figures, unnecessary detail has been omitted for the sake of simplicity of representation.

In step 402, an absorbent pad 31 is disposed within one of the two compartments (not shown) of the barrier bag 400. Thereafter, in step 404, perishable goods 15 (such as, e.g., red meat) are disposed on top of the absorbent pad 31. Thereafter, the package may then be weighed and labeled.

In step 406, a source of non-oxidizing gas, such as particulate carbon dioxide 108, may be added to the other of the two compartments (not shown) of the barrier bag 100. Thereafter, in step 408, the barrier bag 100 is evacuated and sealed to form seals 117/119. After sealing, the sealed bag is then shipped to in step 410.

Referring to FIG. 9B, the shipped bag is received in step 412. It should be noted that, during shipping, the solid carbon dioxide 108 has sublimated and in no longer present in such particulate form within the barier bag 100.

In step 414, the sealed barrier bag 100 is opened, and the absorbent pad 31/perishable goods 15 are removed from the bag. In step 416, the absorbent pad 31 and/or the perishable goods 15 are placed within a tray 30 which is overwapped with film 18 in step 418 to form the final wrapped product 420. The product 420 may be weighed and labeled.

FIG. 10 is a side view of final product 420 on which has been affixed a label 422.

It is to be understood that the aforementioned description is illustrative only and that changes can be made in the apparatus, in the ingredients and their proportions, and in the sequence of combinations and process steps, as well as in other aspects of the invention discussed herein, without departing from the scope of the invention as defined in the following claims. 

I claim:
 1. A packaging system for preserving perishable items which comprises a barrier bag, wherein said barrier bag comprises a first compartment, a second compartment, sealed means for closing one end of the first compartment, sealed means for closing one end of the second compartment, a non-oxidizing gas disposed within said first compartment, a perishable item disposed within said second compartment, means for flowing said non-oxidizing gas from said first compartment to said second compartment, and means for venting said non-oxidizing gas from said second compartment.
 2. The packaging system as recited in claim 1, wherein said means for flowing said non-oxidizing gas from said first compartment to said second compartment is an orifice communicating with said first compartment and said second compartment.
 3. The packaging system as recited in claim 2, wherein said sealed means for closing said one end of said first compartment is a first heat seal.
 4. The packaging system as recited in claim 3, wherein said sealed means for closing said one end of said second compartment is a second heat seal.
 5. The packaging system as recited in claim 4, wherein said non-oxidizing gas is selected from the group consisting of carbon dioxide, nitrogen, and mixtures thereof.
 6. The packaging system as recited in claim 5, wherein said non-oxidizing gas is carbon dioxide.
 7. The packaging system as recited in claim 5, wherein said non-oxidizing gas is nitrogen.
 8. The packaging system as recited in claim 5, wherein said non-oxidizing gas is a mixture of carbon dioxide and nitrogen.
 9. The packaging system as recited in claim 5, wherein said means for venting said non-oxidizing gas from said second compartment is a pressure relief valve.
 10. The packaging system as recited in claim 9, comprising means for venting said non-oxidizing gas from said second compartment when the pressure within said second compartment is from about 0.05 to about 10 pounds per square inch gauge.
 11. The packaging system as recited in claim 10, wherein said barrier bag is comprised of biaxally oriented nylon film coated with an oxygen barrier coating.
 12. The packaging system as recited in claim 11, wherein said oxygen barrier coating is polyvinylidene chloride.
 13. The packaging system as recited in claim 10, wherein said barrier bag is a heat shrinkage barrier bag.
 14. The packaging system as recited in claim 10, wherein said barrier bag has an oxygen permeability of less than about 5 cubic centimeters per 100 square inches per 24 hours.
 15. The packaging system as recited in claim 14, wherein from about 10 to about 150 grams of solid carbon dioxide is disposed within said first compartment.
 16. The packaging system as recited in claim 15, wherein substantially no air is disposed within said first compartment.
 17. The packaging system as recited in claim 16, wherein substantially no air is disposed within said second compartment. 